Prediction of Austenite Grain Growth During Hot Rolling of 0.028% Nb Steel
(Centre for Graduate Studies, Universiti Malaysia Perlis, No. 112 & 114 (First Floor), Block A Taman Pertiwi Indah Jalan Kangar - Alor Setar, Seriab 01000, Kangar Perlis, MALAYSIA, 2010-10)
Effects of rolling temperatures and deformation on the grain growth predictions of hot rolled Nb Steel (A572 Grade 50) were investigated. Hot rolling process was conducted by using a laboratory hot rolling mill, in which ...
MODIFIKASI METODE ETSA TERHADAP PENAMPAKAN BATAS BUTIR FASA AUSTENIT PADA BAJA HSLA A572 GRADE 50 HASIL CANAI PANAS
(SEMINAR NASIONAL METALURGI DAN MATERIAL KE-4 (SENAMM IV) 2010 FAKULTAS TEKNIK UNIVERSITAS SULTAN AGENG TIRTAYASA, 2010-07)
Dalam penelitian ini digunakan baja HSLA A572 Grade 50 dengan kadar Karbon 0,0085 wt% dan Niobium 0,028 wt<'/o. Sampel dipanaskan sampai temperatur 1150°C dan ditahan selama 10 menit, lalu dideformasi panas ...
STUDI PARAMETER PERSAMAAN KONSTITUTIF BAJA HSLA PADA UJI TARIK PANAS REGANGAN BIDANG
(Deputi Teknologi Industri Rancang Bangun & Rekayasa Badan Pengkajian dan Penerapan Teknologi Jakarta, 2011-12)
Uji tarik panas merupakan salah satu metode pengujian yang dilakukan untuk mengevaluasi sifat mekanis, sifat plastisitas material dan sifat perpatahan selama proses pembentukan logam. Pengujian ...
PERBEDAAN NILAI KEKERASAN PADA PROSES HARDENING DAN DOUBLE TEMPERING BAJA PERKAKAS SKD 11
(Jurusan Teknik Mesin Fakultas Teknik Universitas Andalas, 2013-07-02)
Uji keras merupakan salah satu metode pengujian yang dilakukan untuk mengevaluasi sifat mekanis baja yang mengalami proses perlakuan panas. Pada penelitian ini dilakukan proses perlakuan hardening baja perkakas ...
PENGARUH MEDIA PENDINGIN DAN TEMPERATUR TERHADAP NILAI KEKERASAN PADA PROSES HARDENING TEMPERING BAJA PERKAKAS SKD II
(Majalah Ilmiah Politeknik Mandiri Bina Prestasi, 2013-06)
Tulisan ini mengungkapkan hasil penelitian tentang nilai kekerasan baja perkakas SKD 11 yang mengalami proses hardening dan tempering. Baja SKD 11 dipanaskan pada temperatur 1050°C dan ditahan selama 2 jam diikuti ...
Effect of Equal Channel Angular Pressing and Post Heating on Microstructure and Hardness of Cu-Zn 70/30
(Advanced Materials Research Vol. 789 (2013) pp 373-378 Online Available since 2013/Sep/04 at www.scientific.net, 2013-09-04)
Severe plastic deformation (SPD) using various pass number of Equal Channel Angular
Pressing (ECAP) experiment and followed heating at 400oC has been done for rod brass Cu-Zn
70/30 to investigate the operation on ...
Uniaxial Tensile Test Subject to Thermo-mechanical Process
(Faculty of Engineering Universitas Indonesia, 2011-07)
Gambaran Profile Kepribadian EPPS Mahasiswa Dengan Permasalahan Akademik Dan Perilaku
(Majalah Ilmiah Fakultas Psikologi - Universitas HKBP Nommensen, 2017-09-01)
Penelitian ini merupakan penelitian kuantitatif deskriptif yang bertujuan untuk melihat gambaran kebutuhan-kebutuhan EPPS pada mahasiswa/i dengan permasalahan akademik dan permasalahan perilaku. Permasalahan akademik ...
Pengaruh Dimensi Kualitas Pelayanan Terhadap Kepuasan Mahasiswa Fakultas Ekonomi Universitas HKBP Nommensen Medan
(Jurnal Ekonomi dan Bisnis Fakultas Ekonomi Universitas HKBP Nommensen, 2012-01)
The aim of the research is to identify the influencing of service quality on student's satisfaction in Faculty Economy of Nommensen University. The number of samples exerted for this analysis amounted 92 srudents. The ...